Boiler steel plate A515 is available in different grades, including A515 Grade 60, A515 Grade 65, and A515 Grade 70. The tensile strength of these grades varies

ASTM A285 grade A steel does not have specific heat treatment requirements outlined in the standard specification. A285 grade A is a low to intermediate tensile

1. Processing technology: This is also one of the factors that cause oxidation of Q345B thick-walled seamless pipes. From the perspective of manufacturing techn

According to the production method, Q345D seamless steel pipe can be divided into: hot rolled seamless pipe, cold drawn pipe, precision steel pipe, thermal expa

The material of Q345B seamless steel pipe is relatively strong and durable. For the rust removal of Q345B seamless steel pipe, it is necessary to master certain

Due to the factors of different regions, environments and climate, the time for forming a stable oxide film on the surface of 09CuPCrNi-A also varies greatly. I

Hot cracks are generated at high welding temperatures. When crystallized, the eutectic with low melting point forms a liquid film, which will lead to cracking u

1. A633 high-strength low-alloy structural steel is an American standard steel plate, which is a normalized high-strength steel, A633 steel plate is very suitab

Several factors can influence the fluctuation in ASTM A285 C steel sheet prices. Here are some key factors:1. Raw Material Costs: Fluctuations in the prices of

Q345B seamless steel pipe belongs to hot-rolled and normalized steel, and its main structure is ferrite + pearlite. Q345B seamless steel pipe has high hardness

1. Raw materials
Some Q345B seamless steel pipe factories will choose round steel produced by small steel factories for processing in order to save costs, but t

(1) The high weld seam reinforcement of Q345B seamless steel pipe makes the primary wave flaw detection impossible, and only the triple wave flaw detection can

Casting Technology
There are two mainstream methods for 42CrMo4 smelting and casting, one is electric arc furnace smelting, secondary refining and vacuum degass

Gas in steel is a general term for gases such as oxygen, nitrogen, and hydrogen in the medium absorbed by steel during smelting, welding, or chemical and electr

After the quenching and tempering treatment of 42CrMo4 steel, the inspectors found several small crack defects when visually inspecting the surface quality of 4

After adding phosphorus, copper, chromium, nickel and other trace elements to the Corten B steel, the surface of the steel will form a dense and highly adhesive protective film

Before weathering treatment, we must consider the following three points:
a.The following conditions are not suitable for weathering treatment of Corten B: (1)

A709Gr50 steel plate is a low-alloy high-strength steel plate and is an American standard steel plate for bridges. A709Gr50 steel plate is widely used in the ma

ST37 is a commonly used grade of carbon steel plate known for its good strength and durability. Here are some key aspects of ST37 steel plate specification:1. S

ST52 steel sheet does not generally require any special fabrication techniques. It can be readily fabricated using standard manufacturing processes and techniqu

Q345B large-diameter seamless steel pipe is a long steel material with a hollow cross-section and no joints that is processed by rolling or cold drawing with se

After the Q345B seamless steel pipe is welded, the thermal hardness test of the weld should be carried out. The evaluation standard is that the thermal hardness

A285 GrC is named according to the content of C (carbon) and Mo (molybdenum), which means that the carbon content of this steel plate is about 0.16%, and the co

In the quenching and cooling process of normal quenching and tempering treatment of 42CrMo4 steel, oil cooling quenching or water quenching oil cooling quenchin

Perhaps you know what kind of material S355N is, but do you know any knowledge about hot rolling and flaw detection of S355N?Hot rolling of S355N steel plate:
S