Inclusions in X70 pipeline steel mainly exist in the form of non-metallic compounds, such as oxides, sulfides, nitrides, etc. Non-metallic inclusions have a gre

In the API 5L steel pipe standard, the quality standards (or requirements) of steel pipes are divided into PSL1 and PSL2. PSL is an abbreviation for product spe

"X" in the X52 stee designation indicates pipeline steel, and "52" indicates that the minimum yield strength value of the steel plate is 52ksi (1ksi=6.895Mpa).

D36 steel plate is a high-strength structural steel used in offshore and marine applications. It is typically used for hull structures and provides excellent we

There are several alternative steel materials to ABS grade A plate, including:1. ASTM A36 steel plate: This is a commonly used mild steel plate that has good st

API 5L generally refers to the implementation standard of pipeline pipes, which include seamless steel pipes and welded steel pipes.The national standard GB/T 9

1.There should be no cracks, scars, folds, air bubbles, inclusions, and visually visible delaminations on the surface of X52 steel plates that are harmful to us

The basic production processes of API 5L X60 pipeline steel mainly include: conventional semi-continuous hot rolling, CSP continuous casting and rolling, medium

Q690D belongs to low-alloy high-strength structural steel, and Q690D can also be called low-temperature-resistant high-strength steel with a yield strength of 6

According to the properties of Q690 steel, the author summarizes the following key points of the welding process:
1.Preheating work. The structural parts of the

In order to obtain good mechanical properties, many high-strength steels use a combination of multiple heat treatment methods. For Q690 steel, the suitable heat

The difference between hot rolling and cold drawing of A53 steel is the difference in production process. The hot rolling of A53 steel is processed at high temp

1. Raw materials
The raw material of A106 steel pipe is steel billet. When making A106 cold-drawn steel pipe, the billet should be dried firs, this is to remove

ASTM A53 is Standard Specification for Pipe, Steel, Black and Hot-Dipped, Zinc-Coated, Welded and Seamless.ASTM A106 is Standard Specification for Seamless Carb

A285 carbon steel is generally considered to be weldable using common welding techniques such as shielded metal arc welding (SMAW), gas tungsten arc welding (GT

A285 grade C is a carbon steel plate used primarily in pressure vessel applications. The thickness range of A285 grade C plate varies depending on the intended

The carbon content of S690QL steel plate does not exceed 0.2%. Due to the strengthening effect of alloy elements, the hardenability of weld seam and welding hea

S690QL steel plate is a high-strength low-alloy steel, commonly used in the manufacture of heavy machinery and equipment, S690QL steel plate is also widely used

Pickling: The process of using acid solution to remove scale and rust on the surface for S690QL steel plate is called pickling. It is a method of cleaning the m

The standard thickness tolerance for steel sheet Q235 varies depending on the specific standard that is being used and the thickness range of the sheet.In China

Steel Q235B is not corrosion-resistant. It is a low carbon structural steel with good strength and durability, but it is prone to corrosion in certain environme

In order to produce high-quality S500MC steel, every step has strict requirements. Let's briefly understand the production process of S500MC steel and focus

Steel plate cutting generally refers to the process of mixing industrial gas and oxygen to reach the cutting temperature, melting, blowing slag and dividing the

A204 is named according to the content of C (carbon) and Mo (molybdenum), which means that the carbon content of this steel plate is about 0.16%, and the conten

The seamlessness of A53 steel pipe is mainly accomplished by tension reduction, which is a continuous rolling process of hollow base metal without mandrel.Under