E36WA3 steel plate supplier, NFA E36WA3 steel mechanical property

E36WA3 steel plate
Steel Category: structural steel
Steel grade: NFA 35-502 E36WA3
Dimension: Thickness 2-460mm, Width 1500-3200mm, Length 6000-12000mm
E36WA3 Steel Description:
E36WA3 is a structural weathering steel which is also referred to as atmospheric corrosion resistant steel. The main alloying elements are chromium nickel and copper with added phosphorous which gives it excellent self protecting qualities. As the steel reacts with elements in the atmosphere, the material forms a layer of rust over time which in essence protects the steel from corrosion.
E36WA3 steel is the Equivalent grades as S355J0WP (1.8945) steel in EN 10025 - 5 : 2004 standard and WR50A steel in BS 4360 standard and also FE510C1K1 steel in UNI standard.
E36WA3 Steel Delivery state:
Hot Rolled, Cold Rolled, Normalized, Quenched, Tempering, Thermal Mechanical Control Process (TMCP), Electroslag Remelting Technical, HIC test.

E36WA3 steel chemical composition

C %	Mn %	Cr %	Si %	CEV %	S %
Max 0.12	Max 1	0.3-1.25	Max 0.75	Max 0.52	Max 0.035
Cu %	P %	N %
0.25-0.55	0.06 - 0.15	Max 0.009

Method of deoxidation FN = rimming steels not permitted.

For long products the P and S content can be 0.005% higher.
The E36WA3 steels may show a Ni content of max. 0,65 %
The max. value for nitrogen does not apply if the chemical composition shows a minimum total Al content of 0,020 % or if sufficient other N binding elements are present. The N binding elements shall be mentioned in the inspection document

E36WA3 steel mechanical property

Grade	Min. Yield Strength Mpa						Tensile Strength MPa			Impact
E36WA3	Nominal Thickness (mm)						Nominal Thickness (mm)			degree	J
Thick mm	≤16	>16 ≤40	>40 ≤63	>63 ≤80	>80 ≤100	>100 ≤150	≤3	>3 ≤100	>100 ≤150	0	27
E36WA3	355	345	….	….	….	….	510-680	470-630	….	0	27

The tensile test values given in the table apply to longitudinal samples; in case of strip and sheet steel of widths of ≥600 mm they apply to transverse samples
If E36WA3 mechanical properties have been significantly modified by heavy coldforming, either stress relief annealing or normalised may be applied. Normalised should also be applied following hotforming outside of the temperature range of 750 - 1.050 °C and after overheating.

BEBON,the most professional E36WA3steel exporter,will offer you the the best E36WA3 steel. If you have any order in E36WA3steel from BEBON, please inquiry us soon.