Quenched and tempered WearTuf 450 wear-resistant steel plate

Introduction to WearTuf 450 wear-resistant steel plate:
WearTuf 450 wear-resistant steel plate is a fully martensitic wear-resistant steel plate that has been quenched or quenched and tempered, with an average Brinell hardness of 450HBW. WearTuf 450 wear-resistant steel plate has good wear resistance, weldability and cold forming performance. Due to its high impact toughness, WearTuf 450 steel plate has good crack resistance during manufacture and use.

Chemical composition of WearTuf 450 wear-resistant steel plate:
Melting composition of molten steel: after grain refinement and full deoxidation treatment, wt%

Thickness	C	Si	Mn	P	S	Cr	Ni	Mo	B	CEV	CET
3.0-12mm	0.20	0.60	1.50	0.025	0.010	0.40	0.10	0.20	0.00	0.40	0.30
12.1-25mm	0.22	0.60	1.50	0.025	0.010	0.60	0.15	0.25	0.00	0.50	0.35
25.1-35mm	0.22	0.70	1.60	0.025	0.010	1.00	0.25	0.30	0.00	0.59	0.38
35.1-60mm	0.23	0.70	1.60	0.025	0.010	1.20	0.25	0.50	0.00	0.66	0.40

Mechanical properties of WearTuf 450 wear-resistant steel plate:

Grade	Yield strength	Tensile strength	Elongation	Impact	Delivery Status	Surface Hardness
WearTuf 450	1100Mpa	1400Mpa	10%	45J/-40℃	Quenching/Quenching+Tempering	425-475HBW

WearTuf 450 wear-resistant steel plate size:
The thickness range of WearTuf 450 wear-resistant steel plate is 3.0-60.0mm. Depending on the thickness of the steel plate, the width can reach 3100mm and the length can reach 18000mm.

Application of WearTuf 450 wear-resistant steel plate:
WearTuf 450 steel plate can be widely used in traditional earth transportation, mining and transportation equipment, such as excavators, tippers, dump trucks, crushers, hammers, conveyors and other mining transportation equipment.